S8022

Only values between 1 and 30 with one decimal place are allowed.

SCHOTT
S8022 - S8022
Thickness
2.0
Reflection factor
0.9099
λ [nm]
200 < 10⁻³
210 < 10⁻³
220 < 10⁻³
230 < 10⁻³
240 < 10⁻³
250 < 10⁻³
260 < 10⁻³
270 < 10⁻³
280 < 10⁻³
290 < 10⁻³
300 < 10⁻³
310 < 10⁻³
320 < 10⁻³
330 < 10⁻³
340 < 10⁻³
350 < 10⁻³
360 < 10⁻³
370 0.005
380 0.018
390 0.040
400 0.065
410 0.096
420 0.120
430 0.141
440 0.163
450 0.188
460 0.221
470 0.262
480 0.316
490 0.380
λ [nm]
500 0.448
510 0.505
520 0.531
530 0.512
540 0.443
550 0.337
560 0.220
570 0.120
580 0.053
590 0.017
600 0.005
610 < 10⁻³
620 < 10⁻³
630 < 10⁻³
640 < 10⁻³
650 < 10⁻³
660 < 10⁻³
670 < 10⁻³
680 < 10⁻³
690 < 10⁻³
700 < 10⁻³
710 < 10⁻³
720 < 10⁻³
730 < 10⁻³
740 < 10⁻³
750 < 10⁻³
760 < 10⁻³
770 < 10⁻³
780 < 10⁻³
790 < 10⁻³
λ [nm]
800 < 10⁻³
810 < 10⁻³
820 < 10⁻³
830 < 10⁻³
840 < 10⁻³
850 < 10⁻³
860 < 10⁻³
870 < 10⁻³
880 < 10⁻³
890 < 10⁻³
900 < 10⁻³
910 < 10⁻³
920 < 10⁻³
930 < 10⁻³
940 < 10⁻³
950 < 10⁻³
960 < 10⁻³
970 < 10⁻³
980 < 10⁻³
990 < 10⁻³
1,000 < 10⁻³
1,010 < 10⁻³
1,020 < 10⁻³
1,030 < 10⁻³
1,040 < 10⁻³
1,050 < 10⁻³
1,060 < 10⁻³
1,070 < 10⁻³
1,080 < 10⁻³
1,090 < 10⁻³
λ [nm]
1,100 < 10⁻³
1,110 < 10⁻³
1,120 < 10⁻³
1,130 < 10⁻³
1,140 < 10⁻³
1,150 < 10⁻³
1,160 < 10⁻³
1,170 < 10⁻³
1,180 < 10⁻³
1,190 < 10⁻³
1,200 < 10⁻³
1,250 < 10⁻³
1,300 < 10⁻³
1,350 < 10⁻³
1,400 < 10⁻³
1,450 < 10⁻³
1,500 < 10⁻³
1,550 < 10⁻³
1,600 < 10⁻³
1,650 0.003
1,700 0.007
1,750 0.016
1,800 0.031
1,850 0.053
1,900 0.083
1,950 0.120
2,000 0.162
2,050 0.207
2,100 0.255
2,150 0.302
λ [nm]
2,200 0.345
2,250 0.387
2,300 0.429
2,350 0.469
2,400 0.506
2,450 0.538
2,500 0.562
2,550 0.577
2,600 0.590
2,650 0.602
2,700 0.606
2,750 0.571
2,800 0.374
2,850 0.213
2,900 0.142
2,950 0.107
3,000 0.086
3,050 0.071
3,100 0.059
3,150 0.050
3,200 0.044
3,250 0.039
3,300 0.037
3,350 0.036
3,400 0.036
3,450 0.037
3,500 0.040
3,550 0.044
3,600 0.049
3,650 0.054
λ [nm]
3,700 0.058
3,750 0.055
3,800 0.044
3,850 0.031
3,900 0.019
3,950 0.009
4,000 0.004
4,050 0.001
4,100 < 10⁻³
4,150 < 10⁻³
4,200 < 10⁻³
4,250 < 10⁻³
4,300 < 10⁻³
4,350 < 10⁻³
4,400 < 10⁻³
4,450 < 10⁻³
4,500 < 10⁻³
4,550 < 10⁻³
4,600 < 10⁻³
4,650 < 10⁻³
4,700 < 10⁻³
4,750 0.001
4,800 0.002
4,850 0.003
4,900 0.003
4,950 0.003
5,000 0.003
5,050 0.002
5,100 0.001
5,150 < 10⁻³
Reflection factor
Pd 0.910
Reference thickness
d [mm] 2
Refractive Indices n
nd (587.6 nm) =

Colorimetric evaluation

Illuminant A(Planck T = 2347K)
d [mm] 1 2 3
x 0.253 0.203 0.178
y 0.498 0.549 0.593
Y 30 16 9
λd [nm] 503 505 508
Pe 0.44 0.55 0.61
Illuminant Planck T = 3200 K
d [mm] 1 2 3
x 0.241 0.196 0.173
y 0.478 0.530 0.577
Y 31 16 10
λd [nm] 502 504 507
Pe 0.44 0.54 0.60
Illuminant D65 (TC = 6504 K)
d [mm] 1 2 3
x 0.196 0.169 0.154
y 0.374 0.432 0.492
Y 37 21 12
λd [nm] 496 500 505
Pe 0.40 0.47 0.51
Density
p [g/cm3] 2.77
Bubble content
Bubble class
Transformation temperature
Tg [°C] 453
Temperature coefficient
Tk [nm/°C]
Chemical Resistance
FR class 0.0
SR class 4.0
AR class 3.0
Thermal expansion
α-30°C/+70°C [10-6/K] 7.8
α20°C/300°C [10-6/K] 8.9
α20°C/200°C [10-6/K]